1.DescriptionYJS-525 is good for shoe sole molding products. They are widely used for manual mold making, shoes molds, plaster models, sole sampling, sand casting, etc.
2. Technical Datasheet
Typical general characteristics | Inspection Method | Value |
Product data (Catalyzed A+B) | YJS-525 |
Hardness | Shore A | 25±2 |
Mix Ratio | A:B | 100:2 |
Color | / | White |
Pot life | 25 °C (77F) | 30-40mins |
Curing time | 25 °C (77F) | 3-4 hours |
Mixed viscosity | mPa.s | 25000±1000 |
Tear-strength | kg/cm | 25±2 |
Tensile-strength | M.pa | 4.0±0.5 |
Elongation | % | 450±50 |
Shrinkage | % | â¤0.2% |
Note: This is a 100A:2B mix ratio product that must be measured by weight. The choosing of suitable hardness should be according to the size and pattern design of the products. If large products and therefore multiple-piece molds are needed by customers, silicone rubber with higher hardness will be required for the molds. Conversely, soft silicon is indispensable for molds with complicated pattern and delicate details. The amount of curing agent admixture depends on the actual need of customers. More will be added for speedy drying and fast release and less when otherwise.
3. FEATURES1.Low viscosity2.great flexibility3.Extra low shrinkage4.Chemical resistance5.release properties6.Easy to work with4.High tear strength5.Heat Resistance6.various color is available7.High reproduction rate
4.AppearancePart A: Silicone rubber is a white liquidPart B: Catalyst is a non-rless liquid, white transparent color.ATT: We can provide fast/medium/slow catalyst of for hot, warm or cold season.
5.SHELF LIFE:When stored at or below 32°C (89.6°F) in the original unopened containers, YJS-5 series Silicone Base and its Curing Agents have a usable life of 10 months.
6.PackageSilicone base:1kg/drum; 20kg/drum;25kg/drum;200kg/drum.Curing Agent: 30g/bottle; 1kg/bottle