Product Introduction
Ship rubber fenders are used world wide for ship-to-ship (STS) transfer operations, terminals, and for all kinds of ships. Since its creation until today, more than millions of fenders have been supplied worldwide both for ship-to-ship and ship-to-dock (STD) operations serving our valuable customers. These fenders play a critical role in the safe operation of ship berthing and mooring.
Characteristic
â— External wear resistance â— Bearing pressure
â— Ageing resistance â— Long service life
â— Good air tightness â— Easy storage
â— Non deformation â— Simple installation
Functions & Applications
â— Installed on the wharf and dock for berthing
â— Installed on the shipboard for berthing
â— Float chamber
â— For moving the cargo
Specificaton of Ship Rubber Fender
| Size | Initial Internal Pressure 50kPa | Initial Internal Pressure 50kPa | |||
Diameter/ Meter | Length /Meter | Energy Absorption /KJ | Reaction Force /KN | Energy Absorption /KJ | Reaction Force /KN |
| 0.5 | 1 | 6 | 64 | 8 | 85 |
| 0.7 | 1.5 | 17 | 137 | 24 | 180 |
| 1.0 | 1.5 | 32 | 182 | 45 | 239 |
| 1.0 | 2.0 | 45 | 257 | 63 | 338 |
| 1.2 | 2.0 | 63 | 297 | 88 | 390 |
| 1.5 | 3.0 | 153 | 579 | 214 | 761 |
| 1.7 | 3.0 | 191 | 639 | 267 | 840 |
| 2.0 | 3.5 | 308 | 875 | 430 | 1150 |
| 2.5 | 4.0 | 663 | 1381 | 925 | 1815 |
| 2.5 | 5.5 | 943 | 2019 | 1317 | 2653 |
| 3.0 | 5.0 | 1050 | 2000 | 1571 | 2709 |
| 3.0 | 6.0 | 1312 | 2488 | 1888 | 3292 |
| 3.3 | 4.5 | 1175 | 1884 | 1640 | 2476 |
| 3.3 | 6.0 | 1675 | 2783 | 2338 | 3652 |
| 3.3 | 6.5 | 1814 | 3015 | 2532 | 3961 |
Outer and Inner Rubber Material Requirements of Ship Rubber Fenders
Test item |
Test method | Required value | |
| Outer rubber | Inner rubber | ||
| 1. Before aging | – | – | – |
| 1.1 Tensile strength | ISO 37:2011 | 18 MPa or more | 10 MPa or more |
| 1.2 Elongation | ISO 37:2011 | 400 % or more | 400 % or more |
| 1.3 Hardness | ISO 7619-1:2010 | 60 ± 10 (Durometer hardness Type A) | 50 ± 10 (Durometer hardness Type A) |
2. After aging |
ISO 188:2011 | Air oven aging, 70°C ± 1°C, 96 h | Air oven aging, 70°C ± 1°C, 96 h |
| 2.1 Tensile strength | ISO 37:2011 | Not less than 80 % of the original property | Not less than 80 % of the origi- nal property |
| 2.2 Elongation | ISO 37:2011 | Not less than 80 % of the original property | Not less than 80 % of the origi- nal property |
| 2.3 Hardness | ISO 7619-1:2010 | Not to exceed the original prop- erty by more than 8 | Not to exceed the original prop- erty by more than 8 |
| 3. Tear | ISO 34-1:2010 | 400 N/cm or more | No requirement |
| 4. Compression set | ISO 815-1:2008 | 30 %(70 ± 1 °C, 22hours) or less | No requirement |
5. Static ozone aging test |
ISO 1431-1:2012 | No cracks after elongation by 20 % and exposure to 50 pa at 40 °C for 96 h |
No requirement |
NOTE If the colour of the outer cover is not black, the material requirements will differ from those in this table. a Parts of ozone per hundred million of air by volume. | |||