Product Description
Silica brick is the acid refractory ,which consist mainly of tridymite, cristobalite, and a small amount of residual quartz and glass ses.
The silica content is 94% or more. It has acid slag corrosion resistance and higher high temperature strength. The load softening start temperature is 1620~1670 °C. Long-term use at high temperatures does not deform. The thermal shock stability is low (heat exchange in water for 1~4 times). This residual expansion will make the joints tight and ensure good air tightness and structural strength of the masonry.
Name
Item | Silica brick for coke oven G-D | Silica brick for hot blast stoves RG-94 | Silica brick for glass furnace BG-95 | Normal Silica brick | |||
GZ-95 | GZ-94 | GZ-93 | |||||
Chemical Competent % | SiO2 | â¥93 | â¥94 | â¥95 | â¥95 | â¥94 | â¥93 |
Al2O3 | â¤1.5 | â¤1.0 | â¤1.0 |
|
|
| |
Fe2O3 | â¤1.5 | â¤1.5 | â¤1.0 |
|
|
| |
CaO | â¤3 |
| â¤2.5 |
|
|
| |
True densityï¼g/cm3 | â¤2.34 | â¤2.34 | â¤2.34 | â¤2.37 | â¤2.38 | â¤2.40 | |
Apparent porosity, % | â¤22 | â¤22 | â¤22 | â¤22 | â¤23 | â¤25 | |
Cold crushing strength, Mpa | â¥35 | â¥35 | â¥35 | â¥30 | â¥25 | â¥20 | |
Refractoriness â | â¥1690 | â¥1710 | â¥1710 | â¥1710 | â¥1710 | â¥1690 | |
Initial soften point under loadï¼âï¼2MPaÃ0.6% | 1650 | â¥1650 | 1650 | â¥1650 | â¥1640 | â¥1620 | |
Creep rateï¼%ï¼ 2MPa·1550âÃ2h |
| â¤1 |
|
|
|
| |
Permanent ange on reheatingï¼% 1450âÃ2h |
| +0.2 |
|
|
|
|