Description:
1. Injection Molding ABS Grade 2. High Flame Retardant: The flame retardant performance of AF312A is excellent. This material is
tested based on diffrent thickness. AF312B reached V0 grade at 2.5mm。 3. Widely Used: This ABS grade is the most widely used flame retardant
ABS.
Applications
APPLICATIONS
Technical Data Sheet
Properties
Test Condition
Test Method
Unit
Typical Value
Physical
Specific Gravity
ASTM D792
-
1.18
Molding Shrinkage (Flow), 3.2mm
ASTM D955
%
0.4~0.7
Melt Flow Rate
220℃/10kg
ASTM D1238
g/10min
60
Mechanical
Tensile Strength, 3.2mm
ASTM D638
@ Yield
50mm/min
kg/cm2
440
Tensile Elongation, 3.2mm
ASTM D638
@ Yield
50mm/min
%
5
@ Break
50mm/min
%
Min 20
Tensile Modulus, 3.2mm
1mm/min
ASTM D638
kg/cm2
22,000
Flexural Strength, 6.4mm
15mm/min
ASTM D790
kg/cm2
700
Flexural Modulus, 6.4mm
15mm/min
ASTM D790
kg/cm2
26,000
IZOD Impact Strength, 6.4mm
ASTM D256
(Notched)
23℃
kg·cm/cm
23
-30℃
kg·cm/cm
8
IZOD Impact Strength, 3.2mm
ASTM D256
(Notched)
23℃
kg·cm/cm
27
-30℃
kg·cm/cm
8
Rockwell Hardness
R-Scale
ASTM D785
-
104
Thermal
Heat Deflection Temperature, 6.4mm
ASTM D648
(Unannealed)
18.6kg
℃
77
4.6kg
℃
84
Vicat Softening Temperature
ASTM D1525
5kg, 50℃/h
℃
84
1kg, 120℃/h
℃
Flammability
UL94
2.5mm
class
V-0
3.0mm
class
V-0
Relative Temperature Index
UL 746B
Electrical
℃
80
Mechanical with Impact
℃
70
Mechanical without Impact
℃
80
for more details contact us