Product Description
1. Product Details
Silica brick is the acid refractory ,which consist mainly of tridymite,
cristobalite, and a small amount of residual quartz and glass phases.
The silica content is 94% or more. It has acid slag corrosion
resistance and higher high temperature strength. The load softening start temperature is 1620~1670 °C. Long-term use at high temperatures does not deform. The thermal shock stability is low (heat
exchange in water for 1~4 times). This residual expansion will make the joints tight and ensure good air tightness and structural strength of the masonry.
2.Features
a.Good acid erosion resistanceb.Refractoriness 1690-1730°Cc.Higher refractoriness under load,above
1620-1680°Cd.Poor Thermal shock resistance,should not be used for the
zone which temperature has rapid changee.Poor Volume stability at high temperature,must set aside
appropriate expansion joint when laying brickf.True density is changed between 2.33-2.42g/cm3,the smaller,
the better
3.Technical Data
Name
Item
Silica brick
for
coke oven
G-D
Silica brick
for
hot blast stoves
RG-94
Silica brick
for
glass furnace
BG-95
Normal Silica brick
GZ-95
GZ-94
GZ-93
Chemical
Competent
%
SiO2
≥93
≥94
≥95
≥95
≥94
≥93
Al2O3
≤1.5
≤1.0
≤1.0
Fe2O3
≤1.5
≤1.5
≤1.0
CaO
≤3
≤2.5
True density,g/cm3
≤2.34
≤2.34
≤2.34
≤2.37
≤2.38
≤2.40
Apparent porosity, %
≤22
≤22
≤22
≤22
≤23
≤25
Cold crushing strength, Mpa
≥35
≥35
≥35
≥30
≥25
≥20
Refractoriness ℃
≥1690
≥1710
≥1710
≥1710
≥1710
≥1690
Initial soften point under
load(℃)2MPa×0.6%
1650
≥1650
1650
≥1650
≥1640
≥1620
Creep rate(%)
2MPa·1550℃×2h
≤1
Permanent linear change on reheating,%
1450℃×2h
+0.2